Temperature and pressure dependence of electrical conductivity in synthetic anorthite

	Temperature and pressure dependence of electrical conductivity in synthetic anorthite
	Haiying Hu; Lidong Dai; Heping Li; Keshi Hui; Jia Li
	2015
发表期刊	Solid State Ionics
卷号	276 期号:1 页码:136-141
摘要	Electrical conductivity measurements of synthetic anorthite were carried out as a function of pressure and temperature by a Solartron-1260 Impedance/Gain phase analyzer in a multi-anvil apparatus. The impedance spectroscopy was performed in a frequency range from 10-1 Hz to 106 Hz. The sample was synthesized at 1673 K in a high temperature furnace. Our experimental results show that (1) a dramatic increase in electrical conductivity with increasing temperature and a slightly decrease in conductivity with increasing pressure at constant temperature, however, the effect of pressure on the conductivity is less pronounced than that of temperature; (2) the activation enthalpy linearly increases with increasing pressure (1.86-1.91 eV) reflecting the mobility of Ca2(+) decreases as the anorthite framework becomes more compressed; (3) the activation energy at atmospheric pressure and activation volume are 1.83 eV and 2.39 cm(3)/mol, respectively; (4) According to these Arrhenius parameters, it is proposed that the possible dominant mechanism of the charge transport in anorthite under experimental conditions is the hopping of Ca2(+) from one near aluminum oxygen site to another; (4) the diffusion coefficient of calcium was calculated from the present conductivity data using Nernst-Einstein equation, and compared with previous experimental results.
关键词	Anorthite Electrical Conductivity Transport Mechanism Diffusivity
学科领域	地球深部物质与流体作用地球化学
收录类别	SCI
语种	英语
文献类型	期刊论文
条目标识符	http://ir.gyig.ac.cn/handle/352002/6034
专题	地球内部物质高温高压实验室_地球内部物质高温高压实验室_期刊论文
推荐引用方式 GB/T 7714	Haiying Hu,Lidong Dai,Heping Li,et al. Temperature and pressure dependence of electrical conductivity in synthetic anorthite[J]. Solid State Ionics,2015,276(1):136-141.
APA	Haiying Hu,Lidong Dai,Heping Li,Keshi Hui,&Jia Li.(2015).Temperature and pressure dependence of electrical conductivity in synthetic anorthite.Solid State Ionics,276(1),136-141.
MLA	Haiying Hu,et al."Temperature and pressure dependence of electrical conductivity in synthetic anorthite".Solid State Ionics 276.1(2015):136-141.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Temperature and pres（646KB）			开放获取	使用许可	浏览下载